Opis proizvoda

In principle, a prepolymer could be formed by reacting diisocyanates with an excess of polyol to produce a polyol functional prepolymer with urethane functionality at its center, but this is not practiced commercially and the term "prepolymer" is always used to refer to polyols terminated with isocyanate functionality. The excess isocyanate is required to prevent molecular weight growth caused by opportunistic chain extension of unreacted polyol reacting with the isocyanate-terminated prepolymer. In practice, chain extension always occurs but can be limited by increasing the ratio of isocyanate to hydroxyl functionality. A true "prepolymer" in this regard would then distill the excess isocyanate from the product. In the case where the excess isocyanate is left in the product, this is referred to as a "quasi-prepolymer". In practice, quasi-prepolymer refers to systems with relatively high levels of free isocyanate (>12%), dok se predpolimer odnosi na sustave s niskim udjelom slobodnih izocijanata (<12%). Overall, over 400 million pounds a year of prepolymer is used commercially for many applications where the advantages of prepolymers can be realized.

Ovaj kvazi-MDI poliuretanski predpolimer na bazi estera sastoji se od tri komponente A/B/C. Komponenta A je kvazi-MDI poliesterski predpolimer koji je završio s izocinatom, komponenta B je poliester poliol, komponenta C je 1,4BDO.

Njegovi kvazi predpolimerni sustavi mogu pružiti određene prednosti u odnosu na konvencionalnije pune prepolimere nudeći predpolimere niže viskoznosti i kurativa, nižu temperaturu materijala za obradu, elastomere višestruke tvrdoće s istim sustavom, kao i bolju brigu o okolišu i zdravlju.

Glavna prednost leži u kratkom vremenu vađenja iz kalupa, što omogućuje povećanu produktivnost.

Prednost

• Izvrsna mehanička svojstva
• Podesiva reaktivnost, tj. izbor katalizatora i omjera smjese
• Prikladno za lijevanje vrlo velikih dijelova
• Održive alternative sustavima koji se mogu suočiti s regulatornim ograničenjima
• Smanjena potrošnja energije za veću održivost

Kvazi-MDI sustavi temeljeni na esterima nude vrhunsku otpornost na habanje i trganje s izvrsnom otpornošću na kemikalije kao što su ugljikovodici, ulja i otapala. Ovi sustavi idealan su izbor za primjene kao što su sita, strugači, svinje, noževi za beton, ploče i vibracijske zdjele.

Tipični pokazatelji:

Artikal	BQ3516-B			BQ3516-A			BQ3516-C
NCO sadržaj/%	16.5±0.2			-			-
Radna temperatura / stupanj	45			70			45
Viskoznost MPa-s	700			730			30
Predpolimer	BQ3516-B
Produživač lanca	BQ3516-A+BQ3516-C
Tvrdoća/Shore A	55	60	65	70	75	80	85	90
BQ3516-B (omjer, težinski)	100	100	100	100	100	100	100	100
BQ3516-A (omjer, težinski)	380	180	160	130	110	100	80	60
BQ3516-C (omjer, težinski)	0	9.1	10	11.4	12.3	12.7	13.6	14.5
Katalizator/ukupna težina/(A+B+C)(%)	0.4	0.4	0.4	0.4	0.3	0.3	0.3	0.3
Temperatura kalupa / stupanj	100
Vrijeme geliranja/min	5	5	5	5	5	4	4	4
Vrijeme vađenja iz kalupa/min	50	35	35	30	30	30	30	30
Vrijeme naknadnog stvrdnjavanja (100 stupnjeva)/h	16

Fizička svojstva

Tvrdoća/Shore A	55	60	65	70	75	80	85	90
Vlačna čvrstoća/MPa	16	36	43	46	48	49	50	50
Istezanje pri prekidu/%	950	600	550	550	550	550	500	500
100% Modul/MPa	1.4	2.2	2.4	3.7	4.6	5.2	6.6	9.6
300% Modul/MPa	1.5	4.2	5.2	7.2	11.4	11.1	14.6	19.2
Snaga kidanja (bez Nicka) /(KN/m)	23	55	66	78	88	98	106	125
Čvrstoća na trganje (s Nickom) /(KN/m)	11	21	29	34	38	44	56	63
Odskok (23 stupnja)/ %	56	50	50	48	47	47	46	44
Gubitak abrazije/mm³/(DIN)	11	12	14	15	15	17	19	22
Kompresija/% (22 sata/70 stupnjeva)	15	17	19	21	24	26	29	32
Specifična težina (25 stupnjeva) (g/cm³)	1.17	1.18	1.19	1.19	1.2	1.21	1.22	1.22